Natural leather grain look with a soft touch that comes in various classic colors.
PVC & Knitted Polyester
|
1.10 mm
|
-
|
137 cm/ 54 inches
|
20.000 Rubs
|
Phthalate Free
|
Parameter | Result | Method | |
Bond Strength | ASTM D751-06 | ||
Breaking Strength | Warp Weft |
min. 50 kgf / 2 inch min. 30 kgf / 2 inch |
ASTM D751-06 |
Tear Strength | Warp Weft |
min. 2 kgf min. 2 kgf |
ASTM D2261-02 |
Elongation | Under 14 kg |
80 – 160 % |
ASTM D751-06 |
Stretch (at 12 kg) | Warp Weft |
10 – 30 % 100 – 200 % |
Society of Auto Engineers / Method J-855 |
Permanent Set | Warp Weft |
Max. 5 % Max. 40 % |
Society of Auto Engineers / Method J-855 |
Grain Retention | 105° C ; 15 min. |
No Loss of Grain |
|
Flexibility | Min. 400.000 Cycles |
ASTM D2097-03 | |
Folding Test | Room Temperature Oven Temp. 60° C |
No Crease Withening |
|
Wear Test | No Excessive Loss of Grain or discoloration |
ASTM D4157-02 | |
Taber Abrasion | CS/10/1000 gm 400 Cycles |
800 Cycles |
ASTM D3389-05 |
Click to download pdf version